    The acid temperature Brick, plates, tubes  
    The honeycomb ceramic regenerator
    release time2013-03-21  released byPingxiang City Jinfeng Chemical Packing Co., Ltd.  attention 8079

    The honeycomb ceramic regenerator

    Regenerative high temperature air combustion (HTAC) double acting with energy saving and environmental protection, compared with the traditional combustion technology, fuel saving 20-50%, oxidation loss decreased by more than 20%, the reduction of NOx emissions by more than 40%, the production efficiency is greatly improved. As one of the key components of the honeycomb regenerator has unit volume heat exchange area, fast heat transfer, flow resistance is small, shallow depth, diathermy heat efficiency higher merit. A square hole, round hole, square hole, six pass and plane, inclined plane, single, double groove wall shape. Our technical staff according to the characteristics of industrial furnace in China and the use of the environment, bold innovation, the first in China to use high temperature above 2000 fused corundum and high purity materials synthesis manufacturing honeycomb regenerator, the baffle brick and regenerative ball. By using the synthetic materials, high refractoriness, refractoriness under load, high slag resistance, good thermal shock stability, fast heat conduction, scour resistance good, let the advantages of major, heat capacity, the service life reaches the level of similar foreign products. In addition, the catalyst added at 600 and CO in the flue gas, HC compound catalytic combustion, improving waste heat recovery and reduce pollution gas emissions, is now being popularized in large area.

    Specifications

    Length * width * height hole hole Gekuan wall thickness wall thickness area opening end shape

    200*100*100 20*9 cavity 8.5 2.3 2.528051

    150*100*100 36*24 square hole phi 3*3 1.1 1.273452

    150*100*100 35*20 six 41 1.268765 square hole

    150*100*100 10*6 six 124 4.021050 square hole

    150*100*100 35*20 six square hole Phi 3.5 1.5 1.557050

    150*100*100 17*13 cavity 7.5 1.2 1.336657

    150*100*100 33*19 41 1.356853 hole

    150*100*100 15*9 cavity 8.5 2.3 2.528051

    150*100*100 38*22 six square hole Phi 3.6 0.9 1.269663

    150*100*100 42*28 square hole phi 2.6*2.6 1 1.181553

    100*100*100 7*6 six 124 4.022452 square hole

    100*100*100 31*31 square hole phi 2.65*2.65 0.55 0.7106567

    100*100*100 24*24 square hole phi 3*3 1.1 1.274152

    100*100*100 23*20 six 41 1.260884 square hole

    100*100*100 10*9 cavity 8.5 2.3 2.528051

    Physical properties

    Properties of materials

    Iolite mullite synthesized mullite corundum mullite corundum mullite zirconia corundum mullite

    Bulk density (g/cm3) 0.6-0.8 0.7-0.9 0.8-1.0 0.9-1.1 0.9-1.15 0.9-1.15

    The coefficient of thermal expansion (20-1000 ) *10-6 0C-1 1.8-2.3 4-5 5-6 5-6.5 5-6.5 5-6

    Specific heat capacity (J (g • K) -1 0.85 0.90 1 1.10 1.15 1.15

    Thermal conductivity (1000 (w (m • K) -1 1 1.10 1.20 1.20 1.30 1.30

    The highest use temperature (1250135014501550 ) 15501550

    A axial compressive strength of /MPa 20 22 22 25 30 30

    B axial compressive strength of /MPa > 8 > 10 > 10 > 12 > 15 > 15

    Chemical properties

    Composition of material

    Iolite mullite synthesized mullite corundum mullite corundum mullite zirconia corundum mullite

    SiO2 42-52 40-50 35-38 25-30 23-28 23-28

    AL2O3 36-40 45-50 60-65 65-70 65-70 65-70

    MgO 12-15 6-9 0.5 0.5 0.5 0.5

    Fe2O3 < 1 < 1 < 1 < 1 < 1 < 1

    K2O+Na2O+CaO < 1.2 < 1.2 < 1.2 < 1.2 < 1.2 < 1.2

    , DER-LEFT: 0px; PADDING-BOTTOM: 0px; MARGIN: 0px; PADDING-LEFT: 0px; PADDING-RIGHT: 0px; FONT-SIZE: 16px; VERTICAL-ALIGN: baseline; BORDER-TOP: 0px; BORDER-RIGHT: 0px; PADDING-TOP: 0px"> square hole Phi 3.6 0.9 1.269663

    150*100*100 42*28 square hole phi 2.6*2.6 1 1.181553

    100*100*100 7*6 six 124 4.022452 square hole

    100*100*100 31*31 square hole phi 2.65*2.65 0.55 0.7106567

    100*100*100 24*24 square hole phi 3*3 1.1 1.274152

    100*100*100 23*20 six 41 1.260884 square hole

    100*100*100 10*9 cavity 8.5 2.3 2.528051

    Physical properties

    Properties of materials

    Iolite mullite synthesized mullite corundum mullite corundum mullite zirconia corundum mullite

    Bulk density (g/cm3) 0.6-0.8 0.7-0.9 0.8-1.0 0.9-1.1 0.9-1.15 0.9-1.15

    The coefficient of thermal expansion (20-1000 ) *10-6 0C-1 1.8-2.3 4-5 5-6 5-6.5 5-6.5 5-6

    Specific heat capacity (J (g • K) -1 0.85 0.90 1 1.10 1.15 1.15

    Thermal conductivity (1000 (w (m • K) -1 1 1.10 1.20 1.20 1.30 1.30

    The highest use temperature (1250135014501550 ) 15501550

    A axial compressive strength of /MPa 20 22 22 25 30 30

    B axial compressive strength of /MPa > 8 > 10 > 10 > 12 > 15 > 15

    Chemical properties

    Composition of material

    Iolite mullite synthesized mullite corundum mullite corundum mullite zirconia corundum mullite

    SiO2 42-52 40-50 35-38 25-30 23-28 23-28

    AL2O3 36-40 45-50 60-65 65-70 65-70 65-70

    MgO 12-15 6-9 0.5 0.5 0.5 0.5

    Fe2O3 < 1 < 1 < 1 < 1 < 1 < 1

    K2O+Na2O+CaO < 1.2 < 1.2 < 1.2 < 1.2 < 1.2 < 1.2